SBS Product List
Voptasch SBS LA3001 / Voptasch SBS L 3300
| Segment | Asphalt and bitumen / Roofing and waterproofing |
| Areas of use | Polymer-bitumen binder (PBB), mastics, sealants |
| Benefits, in relation to segments/processing methods | High asphalt concrete strength |
| Mass fraction of volatile substances (%), NMT | - |
| Bound styrene content (%) | 28.5–31.5 |
| Breaking elongation (%), NLT | ≥ 700 |
| Kinematic viscosity of 5.23% solution in toluene at temperature of (25 ±0.1) °C, cSt | 14 ±5 |
| Melt flow index, 190 °C/5 kgf (g/10 min) | < 1 |
| Nominal tensile strength (MPa) | ≥ 14.7 |
| Elasticity modulus 300% (MPa) | ≥ 2.7 |
| Shore A hardness (c.u.) | 80 ±3 |
| Principal characteristics | High crack resistance, resistance to rutting, excellent manufacturability |
| Additional parameters | - |
Voptasch SBS LAP 3001
| Segment | Cable insulation |
| Areas of use | Footwear, cable, household articles |
| Benefits, in relation to segments/processing methods | High absorption rate and oil distribution quality |
| Mass fraction of volatile substances (%), NMT | ≤ 0.8 |
| Bound styrene content (%) | 30±1.5 |
| Breaking elongation (%), NLT | ≥ 700 |
| Kinematic viscosity of 5.23% solution in toluene at temperature of (25 ±0.1) °C, cSt | 14 ±5 |
| Melt flow index, 190 °C/5 kgf (g/10 min) | - |
| Nominal tensile strength (MPa) | ≥ 14.7 |
| Elasticity modulus 300% (MPa) | ≥ 2.7 |
| Shore A hardness (c.u.) | 80 ±3 |
| Principal characteristics | High porosity, medium thermal stability, high mechanical properties |
| Additional parameters | OIT — 187 °C |
Voptasch SBS LK3001
| Segment | Automotive components |
| Areas of use | Road markings |
| Benefits, in relation to segments/processing methods | High absorption rate and oil distribution quality, increased wear resistance, thermal stability |
| Mass fraction of volatile substances (%), NMT | ≤ 0.8 |
| Bound styrene content (%) | 28.0–32.0 |
| Breaking elongation (%), NLT | ≥ 700 |
| Kinematic viscosity of 5.23% solution in toluene at temperature of (25 ±0.1) °C, cSt | 16 ±5 |
| Melt flow index, 190 °C/5 kgf (g/10 min) | < 1 |
| Nominal tensile strength (MPa) | - |
| Elasticity modulus 300% (MPa) | - |
| Shore A hardness (c.u.) | 77±5 |
| Principal characteristics | Increased thermal stability, high porosity, improved mechanical properties |
| Additional parameters | OIT — 204 °C |
Voptasch SBS L 7137
| Segment | Roofing and waterproofing |
| Areas of use | Self-adhesive roofing and waterproofing materials |
| Benefits, in relation to segments/processing methods | Low viscosity, high stickiness and adhesion |
| Mass fraction of volatile substances (%), NMT | ≤ 0.5 |
| Bound styrene content (%) | 32 ±1.5 |
| Breaking elongation (%), NLT | ≥ 600 (up to 1000–1100) |
| Kinematic viscosity of 5.23% solution in toluene at temperature of (25 ±0.1) °C, cSt | - |
| Melt flow index, 190 °C/5 kgf (g/10 min) | 7.0 ±2.0 |
| Nominal tensile strength (MPa) | ≥ 3.0 (up to 4.0–4.5) |
| Elasticity modulus 300% (MPa) | - |
| Shore A hardness (c.u.) | 72–82 |
| Principal characteristics | Produced without the use of BHT |
| Additional parameters | - |
Voptasch SBS L 2237
| Segment | Automotive components |
| Areas of use | Transparent compounds, modification of plastics, adhesives |
| Benefits, in relation to segments/processing methods | - |
| Mass fraction of volatile substances (%), NMT | - |
| Bound styrene content (%) | 27.5 – 30.5 |
| Breaking elongation (%), NLT | ≥800 |
| Kinematic viscosity of 5.23% solution in toluene at temperature of (25 ±0.1) °C, cSt | - |
| Melt flow index, 190 °C/5 kgf (g/10 min) | 3–9 |
| Nominal tensile strength (MPa) | >10.0 |
| Elasticity modulus 300% (MPa) | - |
| Shore A hardness (c.u.) | - |
| Principal characteristics | - |
| Additional parameters | - |
Voptasch SBS L 7147
| Segment | Roofing and waterproofing |
| Areas of use | Self-adhesive roofing and waterproofing materials |
| Benefits, in relation to segments/processing methods | Low viscosity, high stickiness and adhesion |
| Mass fraction of volatile substances (%), NMT | ≤ 0.5 |
| Bound styrene content (%) | 36.0–38.0 |
| Breaking elongation (%), NLT | ≥ 250 |
| Kinematic viscosity of 5.23% solution in toluene at temperature of (25 ±0.1) °C, cSt | - |
| Melt flow index, 190 °C/5 kgf (g/10 min) | 16.0–25.0 |
| Nominal tensile strength (MPa) | ≥1.7 |
| Elasticity modulus 300% (MPa) | - |
| Shore A hardness (c.u.) | 80–92 |
| Principal characteristics | High manufacturability, low viscosity; produced without the use of BHT |
| Additional parameters | Diblock copolymer content – 65-75%. Dynamic viscosity at 25 °C, 25% r-r in toluene — approx. 400 MPa °C |
Voptasch SBS L 2470
| Segment | Automotive components |
| Areas of use | Compounds with improved mechanical characteristics, Increased impact resistance of plastics, adhesives |
| Benefits, in relation to segments/processing methods | - |
| Mass fraction of volatile substances (%), NMT | - |
| Bound styrene content (%) | 38.5 – 41.5 |
| Breaking elongation (%), NLT | ≥550 |
| Kinematic viscosity of 5.23% solution in toluene at temperature of (25 ±0.1) °C, cSt | - |
| Melt flow index, 190 °C/5 kgf (g/10 min) | 3–11 |
| Nominal tensile strength (MPa) | >17.0 |
| Elasticity modulus 300% (MPa) | - |
| Shore A hardness (c.u.) | - |
| Principal characteristics | - |
| Additional parameters | - |
Voptasch SBS RA3000 / Voltronic SBS R 3300
| Segment | Automotive components |
| Areas of use | Polymer-modified bitumen roofing and waterproofing materials |
| Benefits, in relation to segments/processing methods | High heat resistance |
| Mass fraction of volatile substances (%), NMT | ≤ 0.8 |
| Bound styrene content (%) | 28.5–31.5 |
| Breaking elongation (%), NLT | ≥ 550 |
| Kinematic viscosity of 5.23% solution in toluene at temperature of (25 ±0.1) °C, cSt | 26 ±4 |
| Melt flow index, 190 °C/5 kgf (g/10 min) | < 1 |
| Nominal tensile strength (MPa) | ≥ 8.0 |
| Elasticity modulus 300% (MPa) | ≥ 2.0 |
| Shore A hardness (c.u.) | 82 ±5 |
| Principal characteristics | High frost resistance, stress-strain properties, manufacturability |
| Additional parameters | - |
Voptasch SBS RAP 3001
| Segment | Household appliances, electronics, toys, tool making / Footwear / Cable insulation |
| Areas of use | Footwear, cable, household articles |
| Benefits, in relation to segments/processing methods | High absorption rate and oil distribution quality |
| Mass fraction of volatile substances (%), NMT | ≤ 0.8 |
| Bound styrene content (%) | 30±1.5 |
| Breaking elongation (%), NLT | ≥ 550 |
| Kinematic viscosity of 5.23% solution in toluene at temperature of (25 ±0.1) °C, cSt | 26 ±4 |
| Melt flow index, 190 °C/5 kgf (g/10 min) | - |
| Nominal tensile strength (MPa) | ≥ 8.0 |
| Elasticity modulus 300% (MPa) | ≥ 2.0 |
| Shore A hardness (c.u.) | 82 ±5 |
| Principal characteristics | Increased thermal stability, high porosity, improved mechanical properties, the greatest effect is achieved when combined with a radial K grade |
| Additional parameters | OIT — 180 °C |
HOW A PRODUCT IS DELIVERED
Voptasch oversees the transportation of cargos connecting suppliers and producers with points of consumption. The Shipping and Chartering Desk at Voptasch arranges transportation issues, both for suppliers and for customers.
It’s our commitment that costumers’ products shall be delivered on requested time and quality.
Our business model relies on being able to deliver products consistently, safely and responsibly. If we were to supply off-specification products we might suffer financial penalties or find them rejected by customers.
The reputational and societal consequences could be even more significant.
Our expertise is matched
by extensive logistical capabilities around the middle East and we are into develop our infrastructure to expand our market.